SnapSpeed PLA Filament (1kg)

Name: SnapSpeed PLA Filament (1kg)
Brand: Snapmaker
SKU: 34064
Price: 22.9 EUR
Availability: OutOfStock
Rating: 4.5 (2 reviews)

€22,90 EUR ~~€26,99~~

Filament Bulk Sale:
Buy 4+ rolls for $16.27 per roll; Buy 8+ rolls for $14.87 per roll (NON-RFID)；
Buy 4+ rolls for $17.99 per roll; Buy 8+ rolls for $16.99 per roll (RFID). Learn more details here.
Product Overview

• RFID functionality is exclusively supported on the U1. Other printer models can use RFID-enabled filaments, but the RFID features will not be available.
• High-speed printing up to 300mm/s with stable output.

• Strong layer adhesion for clean, solid prints.

• Smooth extrusion and fine surface finish.

• Tough and durable for functional use.

• Tangle-free, clog-free, precision feeding every time.

• Easy to use and widely compatible.

• Eco-friendly material and packaging.

Applicability

• 3D Printing

Compatibility

• Snapmaker U1

• Snapmaker Artisan

• Snapmaker 2.0

• Snapmaker J1/ J1s

• Snapmaker Original

• Widely compatible with most FDM printers.

Learn More Hide

Filament Bulk Sale

As low as €15.62/roll (4 rolls) and €14.27/roll (8 rolls)!

4% off

Matte PLA Filament (1kg)

€22,90 €23,99

RFID / Carbon Black (000000)

RFID / Ash Grey (9B9EA0)

RFID / Sunburst Yellow (F0BE02)

Non-RFID / Lava Orange (F78E0E)

Non-RFID / Pine Green (519F61)

Non-RFID / Engine Red (DE1619)

Non-RFID / Celestial Blue (8BD5EE)

21% off

Basic PLA Filament (1kg)

€22,90 €28,99

21% off

PETG Filament (1kg)

€22,90 €28,99

21% off

ABS Filament (1kg)

€22,90 €28,99

Payment methods

Delivery

Orders will be shipped in 1-3 business days.

Free shipping on orders over €89 (U1 excluded).
VAT INCLUSIVE & EU local warehouse delivery in 3-7 business days.

Snapmaker SnapSpeed PLA

High Speed

Stable Performance

Easy Print

Snapmaker SnapSpeed PLA

High Speed, High Stability

Optimized fluid dynamics enable speeds up to 300mm/s while ensuring smooth, high-quality prints.

Optimized Layer Adhesion

Strong layer adhesion ensures firm bonding and flawless prints, even at high speeds.

Smoother Prints, Finer Finish

SnapSpeed PLA ensures smooth extrusion and optimized cooling for sleek,
detailed prints with a refined finish, even at high speeds.

Tougher Than Ever

Engineered for durability and strength. Perfect for functional parts and prototypes.
Resilient in the face of everyday use.

Precision at High Speeds

Bubble-free vacuum spools feed flawlessly. Anti-clog heat control eliminates jams and flow breaks. Tangle-to-tip precision.

Sustainably Made, Responsibly Used

SnapSpeed PLA is made from 100% renewable plant-based resources and packaged with fully biodegradable cardboard spools, offering a safer choice for both users and the environment.

Specifications

RECOMMENDED PRINTING CONDITIONS5

*Based on a 0.4mm nozzle. Printing conditions may vary with different nozzle diameters.

Nozzle temperature

Classic: 190–210 °C
High-speed: 210–230 °C

Build plate temperature

25–60 °C

Build surface treatment

Glue when needed

Printing speed

Classic: 50-100mm/s
High-speed: 100-300mm/s

Drying setting

55°C for 6h

PHYSICAL PROPERTIES

Density

1.23g/cm³ at 21.5°C

Melt index

15.4 g/10min

THERMAL PROPERTIES

Glass transition temperature

59°C

Melting temperature

164°C

Crystallization temperature

96°C

Decomposition temperature

370°C

Vicat softening temperature

61°C

Heat deflection temperature (ISO 75 1.8MPa)

52°C

Heat deflection temperature (ISO 75 0.45MPa)

53°C

MECHANICAL PROPERTIES - Classic Speed

*Based on 0.4mm nozzle and 0.2mm layer thickness. Classic prirhting speed = 46.7mm/s, printing temperature = 210 °C

Young's modulus (X-Y)

2878.3±74.3 MPa

Young's modulus (Z)

2689.8±92.0 MPa

Tensile strength (X-Y)

46.0±0.5 MPa

Tensile strength (Z)

37.3±0.7 MPa

Elongation at break

21.5±5.02%

Elongation at break (Z)

4.2±2.0%

Bending modulus (X-Y)

2868.2±78.4 MPa

Bending strength (X-Y)

76.5±0.9 MPa

Charpy impact strength (X-Y)

6.1±0.6 kJ/m²

MECHANICAL PROPERTIES - High Speed

*Based on 0.4mm nozzle and 0.2mm layer thickness. High printing speed = 300mm/s, printing temperature = 230 °C

Young's modulus (X-Y)

2649.7±78.3 MPa

Young's modulus (Z)

2433.4±79.4 MPa

Tensile strength (X-Y)

43.9±0.4 MPa

Tensile strength (Z)

32.4±0.4 MPa

Elongation at break

15.1±3.9%

Elongation at break (Z)

3.3±0.5%

Bending modulus (X-Y)

2797.9±40.7 MPa

Bending strength (X-Y)

71.4±0.6 MPa

Charpy impact strength (X-Y)

5.0±0.5 kJ/m²

RECOMMENDED PRINTING CONDITIONS

*Based on a 0.4mm nozzle. Printing conditions may vary with different nozzle diameters.

Nozzle temperature

Classic: 190–210 °C
High-speed: 210–230 °C

Build plate temperature

25–60 °C

Build surface treatment

Glue when needed

Printing speed

Classic: 50-100mm/s
High-speed: 100-300mm/s

Drying setting

55°C for 6h

PHYSICAL PROPERTIES

Density

1.23g/cm³ at 21.5°C

Melt index

15.4 g/10min

THERMAL PROPERTIES

Glass transition temperature

59°C

Melting temperature

164°C

Crystallization temperature

96°C

Decomposition temperature

370°C

Vicat softening temperature

61°C

Heat deflection temperature (ISO 75 1.8MPa)

52°C

Heat deflection temperature (ISO 75 0.45MPa)

53°C

MECHANICAL PROPERTIES - Classic Speed

*Based on 0.4mm nozzle and 0.2mm layer thickness. Classic prirhting speed = 46.7mm/s, printing temperature = 210 °C

Young's modulus (X-Y)

2878.3±74.3 MPa

Young's modulus (Z)

2689.8±92.0 MPa

Tensile strength (X-Y)

46.0±0.5 MPa

Tensile strength (Z)

37.3±0.7 MPa

Elongation at break

21.5±5.02%

Elongation at break (Z)

4.2±2.0%

Bending modulus (X-Y)

2868.2±78.4 MPa

Bending strength (X-Y)

76.5±0.9 MPa

Charpy impact strength (X-Y)

6.1±0.6 kJ/m²

MECHANICAL PROPERTIES - High Speed

*Based on 0.4mm nozzle and 0.2mm layer thickness. High printing speed = 300mm/s, printing temperature = 230 °C

Young's modulus (X-Y)

2649.7±78.3 MPa

Young's modulus (Z)

2433.4±79.4 MPa

Tensile strength (X-Y)

43.9±0.4 MPa

Tensile strength (Z)

32.4±0.4 MPa

Elongation at break

15.1±3.9%

Elongation at break (Z)

3.3±0.5%

Bending modulus (X-Y)

2797.9±40.7 MPa

Bending strength (X-Y)

71.4±0.6 MPa

Charpy impact strength (X-Y)

5.0±0.5 kJ/m²

SnapSpeed PLA Filament (1kg)

As low as €15.62/roll (4 rolls) and €14.27/roll (8 rolls)!

Matte PLA Filament (1kg)

Basic PLA Filament (1kg)

PETG Filament (1kg)

ABS Filament (1kg)

Snapmaker SnapSpeed PLA

Snapmaker SnapSpeed PLA

High Speed, High Stability

Optimized Layer Adhesion

Smoother Prints, Finer Finish

Tougher Than Ever

Precision at High Speeds

Sustainably Made, Responsibly Used